Products
- Tool Parts[10]
- Other Cutting & Forming Tools[6]
- Hammer[1]
- Other Machine Tools Accessories[10]
- Abrasive Tools[2]
- Saw[3]
- Paper Processing Machinery Parts[1]
- Other Machinery[2]
- Woodworking Machinery Parts[1]
- Packaging Machinery Parts[2]
- Other Mechanical Parts[2]
- Metal Processing Machinery Parts[8]
- Saw Blade[7]
- Abrasives[1]
- Tool Holder[2]
- Turning Tool[1]
- Food Processing Machinery Parts[1]
- Other Hardware[1]
- Drill Bit[9]
- Electric Drill[1]
- Other Tools[3]
- Knife[1]
- Square Steel[1]
- Other Steel Products[1]
- Steel Round Bars[10]
- Flat Steel[2]
- Metal Building Materials[1]
- Steel Sheets[3]
Contact Us
- Contact Person : Ms. luo nancy
- Company Name : Shanghai Sincere Steel & Tools Co., Ltd.
- Tel : 86-21-58798715
- Fax : 86-21-58793451
- Address : Shanghai,Shanghai,Suite 1513, Lucky Mansion, 660 Shangcheng Road, Pudong New Area, Shanghai City. China
- Country/Region : China
- Zip : 200120
die steel
Product Detailed
Related Categories:Steel Round Bars
round bar steel:H13(size20mm-400mm),D2(size20mm-160mm),H11(size20-400mm,H10(size20-250mm),SKD11(size20-160mm)
round bar steel:H13(size20mm-400mm),D2(size20mm-160mm),H11(size20-400mm,H10(size20-250mm),SKD11(size20-160mm),1.2367(size20-250mm)
| Cold work Die steel | ||||||||||
| Cr12Mo1V1 | ||||||||||
| Similar to other Foreign Grade | GB | ASTM | DIN | JIS | ||||||
| Cr12MoS1V1 | D2 | 1.2379 | SKD-11 | |||||||
| Chemical composition% | Standard | C | Mn | Si | Cr | Mo | V | S | P | |
| GB/T1299 | 1.4/1.6 | ≤0.6 | ≤0.4 | 11.0/13.0 | 0.7/1.2 | 1.5/1.1 | ≤0.03 | ≤0.03 | ||
| Description | High Hardenability,Hardness and high wear resistance ,small deformation .Compare with Cr12*CrW12 ,had higher heghness ,but hardness to a certain degree ,Made reasonably for complicated sections | |||||||||
| Application | Various cold work tools and dies,such as cold punch,cold shear,ect | |||||||||
| Heat treatment | Hardening usual:980-1040oC oil or air blast HRC64-62 preheating twice(500-850oC) | |||||||||
| Tempering for stress relieving and obtain stable structure 180-200oC hold≥2hoursHRC63-62 | ||||||||||
| Tempering HRC adjust to oC(Refer) | ||||||||||
| 180-200oC | 250oC | 300oC | 450oC | |||||||
| 62-63 | 62 | 61 | 59 | |||||||
| Annealing:780-800 oCslow cooling | ||||||||||
| Size and shape | Bars:ø15-200mm Flats:20-80*200-600mm | |||||||||
| Delivery condition | Annealed hardness HB≤255 | |||||||||
| Hot work Die steel | ||||||||||
| 4Cr5MoSiV1 | ||||||||||
| Similar to other Foreign Grade | GB | ASTM | DIN | JIS | ||||||
| 4Cr5MoSiV1 | H13 | 1.2344 | SKD-61 | |||||||
| Chemical composition% | Standard | C | Mn | Si | Cr | Mo | V | S | P | |
| GB/T1299-2000 | 0.32/0.45 | 0.2/0.5 | 0.8/1.2 | 4.75/5.5 | 1.1/1.75 | 0.8/1.2 | ≤0.03 | ≤0.03 | ||
| Description | Hardening in air ,Featuring a fine combination of hot strength,heat cracking resistance and impact toughness in work 600 oC.ESR products has macrostructure well EFER steel had cleanlingness evidently ERS and EFER had all higher iso directivity | |||||||||
| Application | Extrusion dies and die-casting for alumium ,Mandgnesium allay mostly ,for copper alloy could use.Mechiaincal press forhing of steel could use also | |||||||||
| Heat treatment | hardening usual 1000-1040oC oil or blast air | |||||||||
| Tempering HRC adjust to oC(Refer) | ||||||||||
| ToC | Hardening | 180-300 oC | 450-500 oC | 550-570 oC | ||||||
| HRC | 53-55 | 51-52 | 53-54 | 50-52 | ||||||
| For stabilization of moulds size tempering toC,as compared work toC,higher usual 25oC. | ||||||||||
| For nelieving stress of machine heade650oC,holded to uniform,cooling in furnace to 500 oCafter air cooling | ||||||||||
| Annealing:800-580oC slow cooling | ||||||||||
| Size and shape | Bars:ø5-400mm Flats:20-80*200-600mm | |||||||||
| Delivery condition | Annealed hardness HB≤235 | |||||||||